Heat Shrinkable Opened Sleeves Heavy Duty
-
$10.00≥1000 Set/Sets
- Min. Order:
- 1000 Set/Sets
- Min. Order:
- 1000 Set/Sets
- Transportation:
- Ocean, Land, Air, Express
- Port:
- Shanghai, Qingdao, Shenzhen
Your message must be between 20 to 2000 characters
Contact Now| Place of Origin: | Sichuan,China |
|---|---|
| Productivity: | 3000 sets per day |
| Supply Ability: | 3000 sets per day |
| Payment Type: | T/T,L/C |
| Incoterm: | CFR,FOB,CIF,EXW,FCA |
| Certificate: | ISO |
| HS Code: | 392010 |
| Transportation: | Ocean,Land,Air,Express |
| Port: | Shanghai,Qingdao,Shenzhen |
Heat Shrinkable Opened Sleeves Heavy Duty
Excellent multi-functional adhesive that allows lower installation in pre-heat temperature and bonding to 3LPE/DFBE/FBE/CTE
Full resistance to shear forces induced by soil and thermal movements.
Superior cathodic disbondment, hot water immersion resistance and Thermal ageing resistance that offers the optimum barrier long term protection against corrosion.
Reduction in time and cost by lower pre-heat temperature, wet epoxy primer application.
Excellent resistance to cathodic disbandment.
Forever Cross Linked Heat Shrinkable Sleeves is a radiation cross linked sleeve designed for corrosion protection of straight pipes, fittings, bends, elbows and other irregular configurations.
When heated the backing layer shrinks and the adhesive flows and forms a reliable corrosion protection seal onto metal and adjacent coating surfaces.
The epoxy primer( Base +Cure) should applied to the prepared pipe surface then heat shrink sleeve is immediately wrapped around the joint over the wet epoxy primer.
Heat Shrinkable Opened Sleeves Heavy Duty Composition
Forever Cross Linked Heat Shrinkable Sleeves consists of three layers, Epoxy primer layer, adhesive layer, film backing.
Epoxy Primer： Liquid epoxy, solvent free two component.
Adhesive: High shear strength co-polymer adhesive
Film backing: Radiation cross linked. High density polyethylene
Heat Shrinkable Opened Sleeves Heavy Duty Features
Excellent resistance to cathodic disbandment.
Long term corrosion protection.
Non hardening and non cracking.
Mechanical protection and moisture resistance.
Excellent chemical resistance
Excellent resistance to shear forces
Fast application and high performance.
Heat Shrinkable Opened Sleeves Heavy Duty Properties
|
Radiation Cross Linked Backing |
||
|
Property |
Typical Value |
Test Method |
|
Tensile Strength |
20MPa（2900 psi） |
ASTM D-638 |
|
Elongation at Break |
550% |
ASTM D-638 |
|
Specific Gravity |
0.95 |
ASTM D-792 |
|
Hardness, Shore D |
52 |
ASTM D-2240 |
|
Dielectric Strength |
30 kv/mm |
ASTM D-149 |
|
Water Absorption |
0.05% |
ASTM D-570 |
|
Shrink Force |
240KPA(35 psi) |
ASTM D-638 |
|
Volume Resistivity |
1.0 x 1016 ohm.cm |
ASTM D-257 |
|
Hot Melt Adhesive |
||
|
Property |
Typical Value |
Test Method |
|
Softening Point |
90℃ |
ASTM E-28 |
|
Lap Shear |
40 psi |
ASTM D-1002 |
|
Pipeline Heat shrinkable Sleeve |
||
|
Property |
Typical Value |
Test Method |
|
Peel to Steel |
75N/cm |
ASTM D-4541 |
|
Low Temperature Flexibility |
-20℃ |
ASTM D-2671 |
|
Cathodic Disbondment |
10mm radius |
ASTM G8,30days,@23℃ |
|
Impact Resistance |
Pass |
DIN EN 12068 |
|
Indentation Resistance |
Pass |
DIN EN 12068 |
|
Dielectric Breakdown |
35kv |
ASTM D-149 |